Multibase C6-135 Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-135 Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 36
36
no post cure; ASTM D2240
50
50
post cured- 2 hours at 177°C; ASTM D2240
50
50
post cured- 4 hours at 177°C; ASTM D2240
50
50
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 8.198 MPa
1189 psi
post cured- 4 hours at 177°C; ASTM D412
8.281 MPa
1201 psi
no post cure; ASTM D412
8.749 MPa
1269 psi
post cured- 2 hours at 177°C; ASTM D412
8.936 MPa
1296 psi
post cured- 8 hours at 177°C; ASTM D412
Tensile Strength, Yield 1.23 MPa
178 psi
at 200%, no post cure; ASTM D412
2.10 MPa
304 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
2.11 MPa
306 psi
200%, post cured- 4 hours at 177°C; ASTM D412
2.14 MPa
310 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 814 %
814 %
post cured- 4 hours at 177°C; ASTM D412
843 %
843 %
post cured- 8 hours at 177°C; ASTM D412
847 %
847 %
post cured- 2 hours at 177°C; ASTM D412
1117 %
1117 %
no post cure; ASTM D412
Tear Strength 35.2 kN/m
201 pli
Die B, no post cure; ASTM D624
35.9 kN/m
205 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
36.3 kN/m
207 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
37.9 kN/m
216 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
Thermal Properties Metric English Comments
Shrinkage 2.4 %
2.4 %
no post cure
2.90 %

@Temperature 177 °C,
Time 7200 sec
 2.90 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
3.00 %

@Temperature 177 °C,
Time 14400 sec
 3.00 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
3.00 %

@Temperature 177 °C,
Time 28800 sec
 3.00 %

@Temperature 351 °F,
Time 8.00 hour
 post cured