Sharadaa Ceramics VELECRETE RC 105 Rodding Castables

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Sharadaa Ceramics
Trade Name VELECRETE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sharadaa Ceramics VELECRETE RC 105 Rodding Castables.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The Rodding Castables offered by us are user friendly in nature and does not require high energy mixing machines and vibrators. Free flowing in nature, these castables are designed in compliance with international standards.Bond: UltrafineAggregate: AndalusiteType of Setting: HydraulicApplication area: Tip casting & Burner PipeInformation provided by Sharadaa Ceramics Pvt. Ltd.
Physical Properties Metric English Comments
Bulk Density 2.10 g/cc
0.0759 lb/in³
After Drying at 110°C
Grain Size <= 8000 µm
<= 8000 µm
Mechanical Properties Metric English Comments
Modulus of Rupture 0.0160 GPa

@Temperature 1000 °C
2.32 ksi

@Temperature 1830 °F
Cold
0.0200 GPa

@Temperature 110 °C
2.90 ksi

@Temperature 230 °F
Cold
0.0200 GPa

@Temperature 1400 °C
2.90 ksi

@Temperature 2550 °F
Cold
0.0200 GPa

@Temperature 1100 °C
2.90 ksi

@Temperature 2010 °F
Hot
Compressive Strength 80.0 MPa

@Temperature 1000 °C
11600 psi

@Temperature 1830 °F
Cold Crushing
100 MPa

@Temperature 110 °C
14500 psi

@Temperature 230 °F
Cold Crushing
100 MPa

@Temperature 1400 °C
14500 psi

@Temperature 2550 °F
Cold Crushing
Thermal Properties Metric English Comments
Thermal Conductivity 1.98 W/m-K

@Temperature 600 °C
13.7 BTU-in/hr-ft²-°F

@Temperature 1110 °F
Hot Face
Maximum Service Temperature, Air 1650 °C
3000 °F
Component Elements Properties Metric English Comments
Al2O3 58 %
58 %
Fe2O3 1.0 %
1.0 %
Descriptive Properties Value Comments
Permanent Linear Change <1.0%
1650°C
Thermal Expansion 0.9
at 1100°C
Thermal Shock Resistance Excellent