Sharadaa Ceramics REFCAST LC95 Low Cement Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST LC95 Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 3.10 g/cc | >= 0.112 lb/in³ | Dried at 110°C |
| Grain Size | <= 6000 µm | <= 6000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0157 GPa @Temperature 110 °C |
2.28 ksi @Temperature 230 °F |
|
| 0.0186 GPa @Temperature 1100 °C |
2.70 ksi @Temperature 2010 °F |
||
| 0.0265 GPa @Temperature 1500 °C |
3.84 ksi @Temperature 2730 °F |
||
| Compressive Strength | 103 MPa @Temperature 110 °C |
14900 psi @Temperature 230 °F |
Cold Crushing |
| 118 MPa @Temperature 1100 °C |
17100 psi @Temperature 2010 °F |
Cold Crushing | |
| 132 MPa @Temperature 1500 °C |
19200 psi @Temperature 2730 °F |
Cold Crushing | |
| 19.6 MPa @Time 86400 sec |
2840 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 2.62 W/m-K @Temperature 400 °C, Time 10800 sec |
18.2 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 2.67 W/m-K @Temperature 600 °C, Time 10800 sec |
18.5 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 2.73 W/m-K @Temperature 800 °C, Time 10800 sec |
18.9 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1800 °C | 3270 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 94 % | >= 94 % | |
| Fe2O3 | <= 0.30 % | <= 0.30 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.2 - 0.2% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -0.9 - 0.9% | 1500°C | |
| Refractoriness | >1820°C | |
| Thermal Expansion | 0.9 | 1000°C, Reversible |
| Water Required to Mix | 4.5 - 5% |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRB 4 Polyamide 6, Halogen Free Flame Retardant
- Polimeri Europa Eraclene® MP 90 C High Density Polyethylene - Injection Molding
- ND Industries 301 Surface Insensitive Instant Superglue
- Overview of materials for Polybutene
- Kingfa HR-527B Modified ABS
- LG Chemical LUPOL GP3200 PP+MF20%
- Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F)
- Total PPR 12232 Random Copolymer Polypropylene
- EMS-Grivory Grivory® TSG-50/4 PA666-GF50
- Ascend Performance Materials Vydyne® R543H BK02 Nylon 66, 43% Glass Reinforced, DAM
Copyright © lookpolymers.com All Rights Reserved