DuPont Teijin Films Melinex® 1311 Polyester Film
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 1311 Polyester Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melinex® 1311 is a clear polyester film with antistatic properties on both surfaces for improved web handling and safety.Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 96.5 MPa | 14000 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 100 MPa | 14500 psi | ASTM D882A |
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882A |
| Film Elongation at Break, TD | 120 % | 120 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.60 | 0.60 | A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % @Temperature 190 °C, Time 300 sec |
4.0 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 1.0 % @Temperature 190 °C, Time 300 sec |
1.0 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 88.2 % @Thickness 0.127 mm |
88.2 % @Thickness 0.00500 in |
TLT; ASTM D1003 |
| 88.4 % @Thickness 0.102 mm |
88.4 % @Thickness 0.00400 in |
TLT; ASTM D1003 | |
| 88.5 % @Thickness 0.0762 mm |
88.5 % @Thickness 0.00300 in |
TLT; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 2.00e+10 ohm @Temperature 25.0 °C |
2.00e+10 ohm @Temperature 77.0 °F |
500 V DC @ 54% RH; ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Versalloy™ HC 9210-55N Thermoplastic Elastomer (TPE)
- LG Chemical SH610S ABS, Excellent Surface, High Impact
- Lucent Polymers TPP-240 Polypropylene, 40% Talc Filled, Impact Modified
- Henkel Hysol EA 9628H Film Adhesive
- Multibase Multi-Flex® A 8814 Black TPE Thermoplastic Elastomer
- DSM Stanyl® TE250F3 (DAM) Nylon 46 15% Glass Reinforced, Heat Stabilized, Flame Retardant (North America)
- Epoxy Technology EPO-TEK® H31LV Electrically Conductive, Silver Epoxy
- Arlon 51946C015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Polyram Polytron P30N07 Polypropylene, 30% Long Glass Fiber, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved