Sharadaa Ceramics REFCAST LC60 Low Cement Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST LC60 Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.60 g/cc | >= 0.0939 lb/in³ | Dried at 110°C |
| Grain Size | <= 6000 µm | <= 6000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0118 GPa @Temperature 110 °C |
1.71 ksi @Temperature 230 °F |
|
| 0.0147 GPa @Temperature 1100 °C |
2.13 ksi @Temperature 2010 °F |
||
| 0.0167 GPa @Temperature 1500 °C |
2.42 ksi @Temperature 2730 °F |
||
| Compressive Strength | 78.5 MPa @Temperature 110 °C |
11400 psi @Temperature 230 °F |
Cold Crushing |
| 93.2 MPa @Temperature 1100 °C |
13500 psi @Temperature 2010 °F |
Cold Crushing | |
| 108 MPa @Temperature 1500 °C |
15600 psi @Temperature 2730 °F |
Cold Crushing | |
| 19.6 MPa @Time 86400 sec |
2840 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.10 W/m-K @Temperature 400 °C, Time 10800 sec |
7.63 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 1.28 W/m-K @Temperature 600 °C, Time 10800 sec |
8.88 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.39 W/m-K @Temperature 800 °C, Time 10800 sec |
9.65 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 60 % | >= 60 % | |
| Fe2O3 | <= 1.5 % | <= 1.5 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.2 - 0.2% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -1.0 -1.0% | 1500°C | |
| Refractoriness | >1804°C | |
| Thermal Expansion | 0.6 | 1000°C, Reversible |
| Water Required to Mix | 4.5 - 5% |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT LF5200-5001 EM Natural Polyolefin, Unspecified
- SABIC Innovative Plastics Cycolac® INP562 ABS+SAN
- PolyOne Geon™ Vinyl Flexible 90042 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Chemicals E2000 Methylene chloride
- SMAC SMACSONIC® Classic EX Noise and Vibration Damping
- Borealis Low Sulfur™ LE0594 Crosslinkable Semiconductive Compound for Shielding of Power Cables
- Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Milled Glass Reinforced, MDI-based 2-Component Liquid System
- CENTROPLAST CENTROTRON GF 15 Polyphenylene sulfide 15% glass fiber
- Huntsman PE2080 Injection Molding Polyethylene (discontinued **)
- Plastcom SLOVASTER® B GF 20 FRL 4 Polybutylene Terephthalate, 20% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant
Copyright © lookpolymers.com All Rights Reserved