Seals Eastern 7182E Fluorocarbon-Elastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Seals Eastern, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 7182E Fluorocarbon-Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formulated AFLAS® high-temperature "sour" oil & gas service. Excellent acid and base resistance.Information provided by Seals Eastern, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 84
>= 84
ASTM D2240, Type A
89
89
AVG; ASTM D2240, Type A
88

@Temperature 200 °C,
Time 1.21e+6 sec
 88

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
89

@Temperature 200 °C,
Time 3.60e+6 sec
 89

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 16.8 MPa
>= 2430 psi
ASTM D412 Method A
21.59 MPa
3131 psi
AVG; ASTM D412 Method A
20.51 MPa

@Temperature 200 °C,
Time 3.60e+6 sec
 2974 psi

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
23.75 MPa

@Temperature 200 °C,
Time 1.21e+6 sec
 3444 psi

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
Tensile Strength, Yield 4.60 MPa
667 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 4.77 MPa
>= 692 psi
Stress at Elongation M50; ASTM D412 Method A
7.715 MPa
1119 psi
AVG Stress at Elongation M50; ASTM D412 Method A
>= 9.31 MPa
>= 1350 psi
Stress at Elongation M100; ASTM D412 Method A
13.95 MPa
2023 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break >= 120 %
>= 120 %
ASTM D412 Method A
174 %
174 %
AVG; ASTM D412 Method A
244 %

@Temperature 200 °C,
Time 3.60e+6 sec
 244 %

@Temperature 392 °F,
Time 1000 hour
 After Dry Heat Aging; ASTM D865
273 %

@Temperature 200 °C,
Time 1.21e+6 sec
 273 %

@Temperature 392 °F,
Time 336 hour
 After Dry Heat Aging; ASTM D865
Tear Strength Test 359
359
(psi); ASTM D624, Die B
Compression Set 21 %

@Temperature 200 °C,
Time 79200 sec
 21 %

@Temperature 392 °F,
Time 22.0 hour
 ASTM D395, Test B
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 2.78 °C
37.0 °F
ASTM D1329
Processing Properties Metric English Comments
Shelf Life 240 Month
240 Month
ASTM D395, Test B
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 68