Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar

Category Metal , Ferrous Metal , Stainless Steel , T 600 Series Stainless Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name UGIMA®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: 630 UGIMA® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect to machinability. The proprietary UGIMA® manufacturing process – developed exclusively by Ugitech – results in a product that increases productivity and tool life, and improves the surface finish on all types of machined parts. 630 UGIMA® provides a good combination of high strength corrosion resistance, and is often the best solution of stainless steel when high strength is required. Parts machined from solution treated bar stock should be heat treated or aged prior to use. No further heat treatment of machined parts is required when using 630 UGIMA® is one of the precipitation hardened conditions as specified.Applications: Fasteners, Shafts, Valve Bodies, Valves, Valve Trim, Fitting, Machined parts, Medical devices, Aircraft components, and Not recommended for vessels containing liquid or gasses at high pressureInformation provided by Schmolz + Bickenbach
Physical Properties Metric English Comments
Density 7.75 g/cc
0.280 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell >= 277
>= 277
1400°F for 2 hrs and 1150°F for 4 hrs
320 - 340
<br>@Thickness <=25.4 mm
 320 - 340
<br>@Thickness <=1.00 in
 Cold Drawn Bars
320 - 340
<br>@Thickness >=25.4 mm
 320 - 340
<br>@Thickness >=1.00 in
 Turned Bars
>= 255
<br>@Treatment Temp. 579.4 °C,<br> Time 14400 sec
 >= 255
<br>@Treatment Temp. 1075 °F,<br> Time 4.00 hour
>= 255
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 255
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
>= 331
<br>@Treatment Temp. 551.7 °C,<br> Time 14400 sec
 >= 331
<br>@Treatment Temp. 1025 °F,<br> Time 4.00 hour
>= 388
<br>@Treatment Temp. 482 °C,<br> Time 3600 sec
 >= 388
<br>@Treatment Temp. 900 °F,<br> Time 1.00 hour
Tensile Strength >= 793 MPa
>= 115000 psi
1400°F for 2 hrs and 1150°F for 4 hrs
1000 - 1140 MPa
<br>@Thickness <=25.4 mm
 145000 - 165000 psi
<br>@Thickness <=1.00 in
 Cold Drawn Bars
1030 - 1170 MPa
<br>@Thickness >=25.4 mm
 150000 - 170000 psi
<br>@Thickness >=1.00 in
 Turned Bars
>= 931 MPa
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 135000 psi
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
>= 1000 MPa
<br>@Treatment Temp. 579.4 °C,<br> Time 14400 sec
 >= 145000 psi
<br>@Treatment Temp. 1075 °F,<br> Time 4.00 hour
>= 1070 MPa
<br>@Treatment Temp. 551.7 °C,<br> Time 14400 sec
 >= 155000 psi
<br>@Treatment Temp. 1025 °F,<br> Time 4.00 hour
>= 1310 MPa
<br>@Treatment Temp. 482 °C,<br> Time 3600 sec
 >= 190000 psi
<br>@Treatment Temp. 900 °F,<br> Time 1.00 hour
Tensile Strength, Yield >= 517 MPa
>= 75000 psi
1400°F for 2 hrs and 1150°F for 4 hrs
>= 862 MPa
<br>@Temperature 1075 °C,<br> Time 14400 sec
 >= 125000 psi
<br>@Temperature 1967 °F,<br> Time 4.00 hour
>= 862 MPa
<br>@Temperature 1150 °C,<br> Time 14400 sec
 >= 125000 psi
<br>@Temperature 2100 °F,<br> Time 4.00 hour
>= 1070 MPa
<br>@Temperature 1025 °C,<br> Time 14400 sec
 >= 155000 psi
<br>@Temperature 1877 °F,<br> Time 4.00 hour
>= 1170 MPa
<br>@Temperature 900 °C,<br> Time 3600 sec
 >= 170000 psi
<br>@Temperature 1650 °F,<br> Time 1.00 hour
793 - 931 MPa
<br>@Strain 0.200 %,<br> Thickness >=25.4 mm
 115000 - 135000 psi
<br>@Strain 0.200 %,<br> Thickness >=1.00 in
 Turned Bars
931 - 1070 MPa
<br>@Strain 0.200 %,<br> Thickness <=25.4 mm
 135000 - 155000 psi
<br>@Strain 0.200 %,<br> Thickness <=1.00 in
 Cold Drawn Bars
Elongation at Yield >= 18 %
>= 18 %
1400°F for 2 hrs and 1150°F for 4 hrs
>= 0.00 %
<br>@Thickness <=25.4 mm
 >= 0.00 %
<br>@Thickness <=1.00 in
 Cold Drawn Bars
>= 12 %
<br>@Thickness >=25.4 mm
 >= 12 %
<br>@Thickness >=1.00 in
 Turned Bars
>= 10 %
<br>@Treatment Temp. 482 °C,<br> Time 3600 sec
 >= 10 %
<br>@Treatment Temp. 900 °F,<br> Time 1.00 hour
>= 12 %
<br>@Treatment Temp. 551.7 °C,<br> Time 14400 sec
 >= 12 %
<br>@Treatment Temp. 1025 °F,<br> Time 4.00 hour
>= 13 %
<br>@Treatment Temp. 579.4 °C,<br> Time 14400 sec
 >= 13 %
<br>@Treatment Temp. 1075 °F,<br> Time 4.00 hour
>= 16 %
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 16 %
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
Reduction of Area >= 55 %
>= 55 %
1400°F for 2 hrs and 1150°F for 4 hrs
>= 40 %
<br>@Thickness >=25.4 mm
 >= 40 %
<br>@Thickness >=1.00 in
 Turned Bars
>= 50 %
<br>@Thickness <=25.4 mm
 >= 50 %
<br>@Thickness <=1.00 in
 Cold Drawn Bars
>= 34 %
<br>@Treatment Temp. 482 °C,<br> Time 3600 sec
 >= 34 %
<br>@Treatment Temp. 900 °F,<br> Time 1.00 hour
>= 45 %
<br>@Treatment Temp. 551.7 °C,<br> Time 14400 sec
 >= 45 %
<br>@Treatment Temp. 1025 °F,<br> Time 4.00 hour
>= 50 %
<br>@Treatment Temp. 579.4 °C,<br> Time 14400 sec
 >= 50 %
<br>@Treatment Temp. 1075 °F,<br> Time 4.00 hour
>= 50 %
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 50 %
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
Modulus of Elasticity 197 GPa
28600 ksi
Tension
Charpy Impact >= 20.3 J
<br>@Treatment Temp. 551.7 °C,<br> Time 14400 sec
 >= 15.0 ft-lb
<br>@Treatment Temp. 1025 °F,<br> Time 4.00 hour
>= 40.7 J
<br>@Treatment Temp. 579.4 °C,<br> Time 14400 sec
 >= 30.0 ft-lb
<br>@Treatment Temp. 1075 °F,<br> Time 4.00 hour
>= 40.7 J
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 30.0 ft-lb
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
>= 74.6 J
<br>@Treatment Temp. 760 °C,<br> Time 7200 sec
 >= 55.0 ft-lb
<br>@Treatment Temp. 1400 °F,<br> Time 2.00 hour
>= 74.6 J
<br>@Treatment Temp. 621 °C,<br> Time 14400 sec
 >= 55.0 ft-lb
<br>@Treatment Temp. 1150 °F,<br> Time 4.00 hour
Thermal Properties Metric English Comments
CTE, linear 10.8 µm/m-°C
<br>@Temperature 20.0 - 200 °C
 6.00 µin/in-°F
<br>@Temperature 68.0 - 392 °F
Thermal Conductivity 34.3 W/m-K
<br>@Temperature 20.0 °C
 238 BTU-in/hr-ft²-°F
<br>@Temperature 68.0 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.070 %
<= 0.070 %
Chromium, Cr 15 - 17.5 %
15 - 17.5 %
Copper, Cu 3.0 - 4.0 %
3.0 - 4.0 %
Iron, Fe >= 70.46 %
>= 70.46 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Nickel, Ni 3.0 - 5.0 %
3.0 - 5.0 %
Niobium, Nb (Columbium, Cb) 0.15 - 0.45 %
0.15 - 0.45 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %
Tantalum, Ta 0.15 - 0.45 %
0.15 - 0.45 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000800 ohm-cm
0.0000800 ohm-cm
Processing Properties Metric English Comments
Annealing Temperature 1040 °C
1900 °F
Hot-Working Temperature 98.9 - 1200 °C
210 - 2190 °F
Then more rapidly
801.7 °C
1475 °F
Slow heating
949 - 1200 °C
1740 - 2190 °F
Forging range
Descriptive Properties Value Comments
Corrosion Resistance Acetic Acid
2/4
Humidity
4/4
NaCl (Saline Mist)
3/4
Nitric Acid
3/4
Sodium Carbonate
2/4