Schmolz + Bickenbach Formadur® 2083 Superclean Plastic Mold Steel

Category Metal , Ferrous Metal , Martensitic , Tool Steel , Mold Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name Formadur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach Formadur® 2083 Superclean Plastic Mold Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Formadur 2083 Superclean is an electro slag remelted (ESR) martensitic stainless steel developed for corrosion resistant applications and Supplied in the annealed conditionCharacteristics: Good corrosion resistance; Good polishability; and High HardnessApplications: Molds for processing corrosive plastics and Extrusion dies for processing corrosive plasticsStress Relieving (Heat Treatment): 1200°F; Cooling: Furnace hold time 2 hours slowly cool in furnace to 920°F and them air cool; Hardness:
Physical Properties Metric English Comments
Density 7.81 g/cc
0.282 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 46

@Treatment Temp. 650.0 °C
 46

@Treatment Temp. 1202 °F
49

@Treatment Temp. 600.0 °C
 49

@Treatment Temp. 1112 °F
54

@Treatment Temp. 300 °C
 54

@Treatment Temp. 572 °F
54

@Treatment Temp. 400 °C
 54

@Treatment Temp. 752 °F
55

@Treatment Temp. 500 °C
 55

@Treatment Temp. 932 °F
56

@Treatment Temp. 550.0 °C
 56

@Treatment Temp. 1022 °F
Tensile Strength 1410 MPa

@Temperature -5.56 °C
 205000 psi

@Temperature 22.0 °F
 45 HRC
1720 MPa

@Temperature -5.56 °C
 250000 psi

@Temperature 22.0 °F
 50 HRC
2000 MPa

@Temperature -5.56 °C
 290000 psi

@Temperature 22.0 °F
 55 HRC
Tensile Strength, Yield 1240 MPa

@Temperature 22.0 °C
 180000 psi

@Temperature 71.6 °F
 45 HRC
1450 MPa

@Temperature 22.0 °C
 210000 psi

@Temperature 71.6 °F
 50 HRC
1550 MPa

@Temperature 22.0 °C
 225000 psi

@Temperature 71.6 °F
 55 HRC
Elongation at Yield 8.0 %

@Temperature 22.0 °C
 8.0 %

@Temperature 71.6 °F
 55 HRC
10 %

@Temperature 22.0 °C
 10 %

@Temperature 71.6 °F
 50 HRC
12 %

@Temperature 22.0 °C
 12 %

@Temperature 71.6 °F
 45 HRC
Thermal Properties Metric English Comments
CTE, linear 11.2 µm/m-°C

@Temperature 21.1 - 93.3 °C
 6.20 µin/in-°F

@Temperature 70.0 - 200 °F
11.5 µm/m-°C

@Temperature 21.1 - 204 °C
 6.40 µin/in-°F

@Temperature 70.0 - 400 °F
11.5 µm/m-°C

@Temperature 21.1 - 288 °C
 6.40 µin/in-°F

@Temperature 70.0 - 550 °F
Thermal Conductivity 22.5 W/m-K

@Temperature 93.3 °C
 156 BTU-in/hr-ft²-°F

@Temperature 200 °F
23.1 W/m-K

@Temperature 149 °C
 160 BTU-in/hr-ft²-°F

@Temperature 300 °F
23.5 W/m-K

@Temperature 204 °C
 163 BTU-in/hr-ft²-°F

@Temperature 400 °F
Component Elements Properties Metric English Comments
Carbon, C 0.42 %
0.42 %
Chromium, Cr 13 %
13 %
Iron, Fe 86.58 %
86.58 %
Processing Properties Metric English Comments
Annealing Temperature 760 - 799 °C
1400 - 1470 °F
Soft; Cooling: Furnace 20°F/hour to 1200 °F/ Then air cooled; < 230 HB