Samsung Cheil Industries Starex® WR-9130 ASA, Unreinforced
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9130 ASA, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 38.2 MPa | 5550 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 56.9 MPa | 8250 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.77 GPa | 256 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm |
2.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- PolyChem Alloy AquaGard™ 4504P
- Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced
- Noltex Soarnol® BS3803 Ethylene Vinyl Alcohol Copolymer
- H.C. Starck Amperit® 519.088 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Multibase Multi-Flex® TPE A 3104-10 AGATE 5ES
- LATI Latiohm 62-03 PD01 G/20 PPA, 20% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East)
- Vicone High Performance Rubber VicoSil™ C240Q-RD High Performance Silicone Rubber
- Chicago Extruded Metals BioBrass® UNS C95520 As-Cast Aluminum Bronze
- Eurotec® Tecoform® PO20 NL RT POM, PTFE modified, natural
Copyright © lookpolymers.com All Rights Reserved