Samsung Cheil Industries Starex® SF-200H Expandable Polystyrene (EPS) FR
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SF-200H Expandable Polystyrene (EPS) FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 - 1.05 g/cc | 1.03 - 1.05 g/cc | |
| Density | 0.0130 g/cc | 0.000470 lb/in³ | Based on 80 times expansion |
| Bead Size | 0.960 - 1.36 mm | 0.0378 - 0.0535 in | JIS Z8801 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 2.10 MPa | 305 psi | @ 15 kg/m<sup>2</sup>; ASTM DC201 |
| Compressive Strength | >= 0.800 MPa | >= 116 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | 6.0 - 7.0 % | 6.0 - 7.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blocking | <1% | |
| Expandability | 80 Times | Expansion for 5 min Cheil Method |
| Fusion | >70% | Cheil Method |
| Polymer Content | 93-94% |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 51 UVT General Purpose Acrylic Resin
- Polymer Resources PEI-GP1-TFE5 Polyetherimide, 5% PTFE, Flame Retardant
- Greene Tweed FLUORAZ® 888 Fluoroelastomer, FEPM
- SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific)
- Styron EMERGEâ„¢ 4530-10 Polycarbonate
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Over-Cured
- Domo 2500H Polypropylene Copolymer
- Braskem Green PE SLH118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- BASF Ultramid® B3L BK00464 PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved