SCG Chemicals EL-Leneâ„¢ L2009F Linear Low Density Polyethylene Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ L2009F Linear Low Density Polyethylene Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE and LDPE to improve tear resistance and seal strengthContains 1000 ppm slip agent and 700 ppm antiblocking agentRecommended Applications:Film for heavy duty bag, industrial bag, rice bag, sugar bag, frozen bagAgricultural filmConstruction filmInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.919 g/cc | 0.919 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C |
>= 1000 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1639 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1200 % | 1200 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 5.71 g/micron | 145 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 370 g/mil | ASTM D1922 |
| Dart Drop | 3.40 g/micron | 86.4 g/mil | ASTM D1709 |
| Dart Drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 37.0 MPa | 5370 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 °C | 252 °F | ASTM D2117 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 16 % | 16 % | ASTM D1003 |
| Gloss | 52 % | 52 % | ASTM D2457 |
Users viewing this material also viewed the following:
- Oxford Polymers ABS 30GF-BK ABS, 30% Glass Fiber Reinforced
- PolyOne Geon™ 210 Series 218 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Arlon 518581R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate (discontinued **)&l
- Techmer ES Plastiblend® ABS 8006
- Trelleborg Emerson & Cuming Eccobond® G 909 One-Component Fast Cure Epoxy Adhesive
- Chevron Phillips EA6740 Rubber Modified Polystyrene
- Fainplast Compounds HAX HF 22G Halogen Free PVC
- China-Yixing Longly Refractories ZTA (20%ZrO2) Zirconia Toughened Alumina Composite Ceramic
- Braskem GM5010T2 HDPE High Density Extrusion Polyethylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 65A
Copyright © lookpolymers.com All Rights Reserved