SCG Chemicals EL-Leneâ„¢ H6105JU High Density Polyethylene Injection Molding

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer	SCG Chemicals Co.
Trade Name	EL-Lene™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SCG Chemicals EL-Leneâ„¢ H6105JU High Density Polyethylene Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Characteristics:Good processabilityWide service temperatureHigh rigidityGood weathering resistance (UV stabilizer)Recommended Applications:Crates for soft drinks, bottles, pallet, garbage bins, containersIndustrial parts for outdoor uses such as motorcycle fendersInformation provided by SCG Chemicals

Physical Properties	Metric	English	Comments
Specific Gravity	0.961 g/cc	0.961 g/cc	ASTM D1505
Environmental Stress Crack Resistance	4.0 hour @Temperature 50.0 Â°C	4.0 hour @Temperature 122 Â°F	F50, 25% Igepal; ASTM D1693
Linear Mold Shrinkage, Flow	0.0169 cm/cm @Thickness 2.00 mm	0.0169 in/in @Thickness 0.0787 in	TPE Method
Linear Mold Shrinkage, Transverse	0.0116 cm/cm @Thickness 2.00 mm	0.0116 in/in @Thickness 0.0787 in	TPE Method
Melt Flow	5.5 g/10 min @Load 2.16 kg, Temperature 190 Â°C	5.5 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	66	66	ASTM D2240
Tensile Strength at Break	29.0 MPa	4210 psi	ASTM D638
Tensile Strength, Yield	23.5 MPa	3410 psi	ASTM D638
Elongation at Break	1100 %	1100 %	ASTM D638
Flexural Modulus	1.27 GPa	185 ksi	ASTM D790
Izod Impact, Notched	>= 0.245 J/cm @Temperature 23.0 Â°C	>= 0.459 ft-lb/in @Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	133 Â°C	271 Â°F	ASTM D2117
Deflection Temperature at 0.46 MPa (66 psi)	75.0 Â°C	167 Â°F	ASTM D648
Vicat Softening Point	127 Â°C	261 Â°F	ASTM D1525
Brittleness Temperature	-60.0 Â°C	-76.0 Â°F	ASTM D746