- SCG Chemicals EL-Leneâ„¢ H5615F High Density Polyethylene Film
SCG Chemicals EL-Leneâ„¢ H5615F High Density Polyethylene Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H5615F High Density Polyethylene Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High speed processingHigh tensile strengthHigh dart impactLow gel contentGood moisture barrierRecommended Applications: Ultra thin film (
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.956 g/cc | 0.956 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C |
>= 1000 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1693 |
| Thickness | 12.0 microns | 0.472 mil | |
| Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | 160 % | 160 % | ASTM D882 |
| Film Elongation at Break, TD | 360 % | 360 % | ASTM D882 |
| Secant Modulus, MD | 0.950 GPa | 138 ksi | ASTM D882 |
| Secant Modulus, TD | 0.980 GPa | 142 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 3.0 g | 3.0 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 118 g | 118 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.250 g/micron | 6.35 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.83 g/micron | 250 g/mil | ASTM D1922 |
| Dart Drop | 8.90 g/micron | 226 g/mil | ASTM D1709 |
| Dart Drop Test | 107 g | 0.236 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 130 °C | 266 °F | ASTM D2117 |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
Users viewing this material also viewed the following:
- Mitsubishi Xantar® 24 R Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 (Asia Pacific)
- DuPont Nucrel® 31001 Ethylene-Acrylic Acid Copolymer Resin for Blown and Cast Film
- Ex-Tech Plastics PerformaTech™ PVC XSD-28 Static Dissipative PVC
- ExxonMobil Mobil Delvac 80W-140 Synthetic Gear Oil
- Dura-Bar G1 Continuously Cast Gray Iron Bar Stock ASTM A48
- Amco PRIMATOP HDPE 004955HP Blow Molding Polyethylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N330 Filler
- Arkema Group KYNAR® 2801-00 Polyvinylidene Fluoride Powder
Copyright © lookpolymers.com All Rights Reserved