SCG Chemicals EL-Leneâ„¢ H5604F High Density Polyethylene Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H5604F High Density Polyethylene Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High tensile strengthHigh dart impactHigh stiffnessLow gel contentGood moisture barrierRecommended Applications: Films for shopping bag, T-shirt bag, garbage bag, liner bagInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.956 g/cc | 0.956 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C |
>= 1000 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1693 |
| Thickness | 12.0 microns | 0.472 mil | |
| Melt Flow | 0.040 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.040 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Elongation at Break, MD | 240 % | 240 % | ASTM D882 |
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 |
| Secant Modulus, MD | 0.800 GPa | 116 ksi | ASTM D882 |
| Secant Modulus, TD | 0.780 GPa | 113 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 3.0 g | 3.0 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.250 g/micron | 6.35 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.67 g/micron | 169 g/mil | ASTM D1922 |
| Dart Drop | 11.6 g/micron | 295 g/mil | ASTM D1709 |
| Dart Drop Test | 139 g | 0.306 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 61.0 MPa | 8850 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 131 °C | 268 °F | ASTM D2117 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ PC-000/10T Polycarbonate (PC)
- Omni Plastics OmniLon™ 6/6 PA6/6 GR15 MF25 Glass/Mineral Filled Nylon
- Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
- Plenco 2408 Phenolic, Granular, Compression Molded
- Crucible Compaction Metals Rene 95 Nickel Based Superalloy
- China Tungsten YG8 Tungsten Carbide for Cutting Tools
- Dow SE SLR-4610 H Solution polymerized Styrene Butadiene Rubber (S-SBR)
- China Tungsten FeMo55-B Ferro Molybdenum
- Arkema Group Orgalloy® LE 6000IH Nylon Alloy, Flexible Grade (Conditioned)
- Shinkong Synthetic Fibers Shinite® PP4210 PP, Fire Retardant
Copyright © lookpolymers.com All Rights Reserved