SABIC Innovative Plastics Valox® VSR4150 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VSR4150 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0080 - 0.010 cm/cm @Thickness 6.40 mm |
0.0080 - 0.010 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 87.0 MPa | 12600 psi | SABIC - Japan Method |
| Elongation at Break | 5.0 % | 5.0 % | SABIC - Japan Method |
| Flexural Strength | 129 MPa | 18700 psi | ASTM D 790 |
| Flexural Modulus | 5.29 GPa | 767 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.590 J/cm @Temperature 23.0 °C |
1.11 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 |
Users viewing this material also viewed the following:
- Chevron Phillips Marlex® D252/257 Linear Low Density Polyethylene Film Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1700-8126 PPO, with glass spheres and PTFE
- Materion BrushCAST® 20CT Fine Grain Casting Alloy (As Cast)
- A. Schulman INVISION™ VX-5170UE Soft Touch Polyolefin Thermoplastic
- China Tungsten ZK10-1 Tungsten Carbide
- Fainplast Compounds Hax™ HFC 087/2 Flame Retardant Polyolefin Cable Compound
- Arkema Group Lacovyl® GB 1040 PVC
- 3M 7742 Polyester Overlaminating Film
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N339 Filler
Copyright © lookpolymers.com All Rights Reserved