SABIC Innovative Plastics Valox® VAC7041 ABS+PBT+PET (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VAC7041 ABS+PBT+PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 6.40 mm |
0.0040 - 0.0060 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 114 MPa | 16500 psi | SABIC - Japan Method |
| Elongation at Break | 8.0 % | 8.0 % | SABIC - Japan Method |
| Flexural Strength | 136 MPa | 19700 psi | ASTM D790 |
| Flexural Modulus | 10.39 GPa | 1507 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® A-1240 HS Polyphthalamide (PPA) Resin, 40% Mineral Reinforced, at 50% RH (d
- Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride (discontinued **)
- Kazanorgsintez 15813-020 High Pressure Polyethylene
- Shuman 502C Black Polypropylene Copolymer
- A. Schulman POLYBATCH™ White 8350 AP Concentrate Based In LDPE
- Elisto THERMOSTAR® HD 550 C Frame Press Insulation Material
- ExxonMobil LDPE LD 250 Low Density Polyethylene Resin (European Grade)
- Phenolic 40%, Carbon fabric 60%
- Overview of materials for Polypropylene with 10% Calcium Carbonate (CaCO3) Filler
Copyright © lookpolymers.com All Rights Reserved