SABIC Innovative Plastics Valox® 732E PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass + Mineral Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 732E PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 1.50 - 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0060 - 0.0080 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D 785 |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.01 J/cm @Temperature 23.0 °C |
1.89 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.2 µm/m-°C @Temperature 60.0 - 138 °C |
14.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.32 @Frequency 1.00e+6 Hz |
3.32 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| 3.53 @Frequency 50.0 - 60.0 Hz |
3.53 @Frequency 50.0 - 60.0 Hz |
ASTM D 150 | |
| Dielectric Strength | 17.9 kV/mm @Thickness 3.20 mm |
455 kV/in @Thickness 0.126 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0080 @Frequency 50.0 - 60.0 Hz |
0.0080 @Frequency 50.0 - 60.0 Hz |
ASTM D 150 |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- Eastman Eastalloy DA106 PC+PET Copolyester/Polycarbonate (discontinued **)
- Saint-Gobain Rulon® E Grade Bearing/Seal PTFE (discontinued **)
- Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (DAM) (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N339 Filler
- ExxonMobil Extra Hecta Super Mobil Cylinder Oil
- Asahi Glass Lumiflon LF-302 Solvent Soluble Fluoropolymer w/ isocyanate hardening agent
- Aremco Corr-Paint™ CP4095-S High Temperature Protective Coating, Silicone-Polyester
- Arlon CP-427R Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved