SABIC Innovative Plastics Ultem UR9076LG PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem UR9076LG PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard flow mineral filled Polyetherimide Blend. Restricted sales to GE Specialty Film & Sheet.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D 792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C |
0.40 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.4 g/10 min @Load 6.60 kg, Temperature 295 °C |
2.4 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
| 10 g/10 min @Load 5.00 kg, Temperature 220 °C |
10 g/10 min @Load 11.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 5 mm/min; ASTM D 638 |
| 3.30 GPa | 479 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.550 J/cm @Temperature 23.0 °C |
1.03 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 49.0 kJ/m² @Temperature 23.0 °C |
23.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 4.90 J/cm² @Temperature 23.0 °C |
23.3 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 854 J @Temperature 23.0 °C |
630 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 77.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 185 °C @Thickness 3.20 mm |
365 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 179 °C | 354 °F | Rate B/50; ISO 306 |
| 182 °C | 360 °F | Rate B/120; ISO 306 | |
| 184 °C | 363 °F | Rate B/50; ASTM D 1525 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ SE11-023E PVC Compound
- Kazanorgsintez 108-276 Low Density Polyethylene Composition with Improved Processibility
- Magyar Aluminum ALO-DFC Alumina
- LG Chemical LUPOY GP1000L PC, Transparent
- Lubrizol Advanced Materials Pearlthane® D91F65D Thermoplastic Polyurethane Elastomer
- Karina 851-48/1-F-IS Black PVC Compound
- Tipco Tipcolite® VASW 150 Phenolic Compound, Glass Fibers & Minerals, Medium-Soft Flow & High Strength
- Eurostar Staramide PF00AE PA6, 50% Glass Fiber Filled, Injection Molded
- 3M 7014FL Performance Paper Label Material
- Solvay Specialty Polymers Veradel® A-304P Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved