SABIC Innovative Plastics ULTEM 4211 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 4211 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Melt Flow | 10.3 g/10 min @Load 6.60 kg, Temperature 337 °C |
10.3 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 129 MPa | 18700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 4.37 J/cm @Thickness 3.20 mm |
8.19 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Intene® 40 AF Butadiene Rubber
- Outokumpu 2205 Duplex Stainless Steel
- NOVA Chemicals Dytherm® 170F Expandable Polystyrene
- Malvern Minerals Trikup® PT Silane Treated Aluminum Hydroxide
- Lubrizol Advanced Materials Pearlthane® ECO D12T55D Thermoplastic Polyurethane
- SABIC Innovative Plastics Noryl EN130S PPE+HIPS (Europe-Africa-Middle East)
- Akzo Nobel Expancel® 051 WU 40 Wet unexpanded microspheres
- Arlon 940-10Rxx-P1 0.040" (1.02 mm) Self-Fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved