SABIC Innovative Plastics ULTEM 1110 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 1110 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.72 GPa | 540 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 16.02 J/cm @Thickness 3.20 mm |
30.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Gardner Impact | 23.0 J | 17.0 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 |
Users viewing this material also viewed the following:
- Pinnacle Polymers 2135 H Medium Impact Polypropylene Copolymer, Injection Molding Grade
- H.C. Starck Amperit® 515.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Stat-kon DEF13 PC
- Hexcel® HexForce™ 1035 Fiber Glass Fabric
- Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE)
- Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness)
- 3M Scotchgard™ 1001MS Protective Film
- Ferro EG 2964 Glaze and Sealant Glass
- H.C. Starck Amperit® 525.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 83-17
Copyright © lookpolymers.com All Rights Reserved