SABIC Innovative Plastics ULTEM 1110 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 1110 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.72 GPa | 540 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 16.02 J/cm @Thickness 3.20 mm |
30.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Gardner Impact | 23.0 J | 17.0 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3780H TPE, PP Overmold or Standalone use
- Pacific Sintered Materials FN-262-T High Strength Nickel Steel Powdered Metal
- SABIC Innovative Plastics Lexan® ML7678 PC
- NextGen Adhesives G907-05 Epoxy Adhesive
- Indium Corp. 16-2212 Flux Thinner
- SABIC Innovative Plastics Valox® IQNH4560 PBT (Asia Pacific)
- Stir SpA AF 84 CZ (PVC)
- 3M 1126 EMI Shielding Tape
- BASF Ultramid® C3U PA66/6 (Conditioned)
- Quantum Composites QC-8704FR 63% Glass Fiber Flame Retardant Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved