SABIC Innovative Plastics Noryl PKN4766 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl PKN4766 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS. Translucent. FDA compliant. High flow. Extrusion. Microwavable. Food packaging uses.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 300 °C |
25 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 10 % | 10 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.93 GPa | 425 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.260 J/cm @Temperature 23.0 °C |
0.487 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Impact Test | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ASTM D 1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT1141 PC (Europe-Africa-Middle East)
- Lucas-Milhaupt Silvaloy® A25T Brazing Alloy
- SABIC Innovative Plastics NORYL TPN9221 PPE+PS (Asia Pacific)
- Teknor Apex APEX® 84853-L Polyvinyl Chloride, Flexible
- CEN® Electronic Material CV Polyimide Film, 4 Mil Thickness
- DuPont Performance Polymers Delrin® 500TL NC010 Acetal Homopolymer (Unverified Data**)
- SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR
- PolyOne Edgetek® UR-30GF/000 Natural Thermoplastic Polyurethane (Ether-Based), 30% Glass Fiber Reinforced (di
Copyright © lookpolymers.com All Rights Reserved