SABIC Innovative Plastics NORYL FN150X PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FN150X PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Improved reliability and productivity. Thin wall capability. UL94 V-0/5VA rated. All data at 20% weight reduction and 0.250"" wall.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa @Thickness 6.35 mm |
4060 psi @Thickness 0.250 in |
ASTM D638 |
| Tensile Strength, Yield | 28.0 MPa @Thickness 6.35 mm |
4060 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 14 % @Thickness 6.35 mm |
14 % @Thickness 0.250 in |
ASTM D638 |
| Elongation at Yield | 7.3 % @Thickness 6.35 mm |
7.3 % @Thickness 0.250 in |
ASTM D638 |
| Flexural Yield Strength | 52.0 MPa | 7540 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 1.74 GPa | 252 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 3.41 J/cm @Thickness 6.40 mm |
6.39 ft-lb/in @Thickness 0.252 in |
ASTM D4812 |
| Taber Abrasion, mg/1000 Cycles | 152 | 152 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C @Thickness 6.40 mm |
163 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 110 °C | 230 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 3.98 mm |
V-0 @Thickness 0.157 in |
UL 94 |
| 5VA @Thickness 3.98 mm |
5VA @Thickness 0.157 in |
UL 94 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - Flame Class Minimum Density | 0.9g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 20% | |
| Radiant Panel Listing | YES | UL Tested |
Users viewing this material also viewed the following:
- Magyar Aluminum ALO-Ex33 Alumina
- Flint Hills P4C5B-030 Homopolymer Polypropylene
- Materion Beryllium Copper Alloy 25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17200)
- Ineos H20A-00 Polypropylene Homopolymer
- Spartech Polycast SAR (Super Abrasion Resistant) Cell Cast Acrylic
- Shinkong Synthetic Fibers Shinite® F202G30 PBT, 30% Glass Filled, Fire Retardant, Halogen Free
- Cossa Polimeri ESTAPROP H 0560 HFC Polypropylene, 30% Glass Filled
- Parker Chomerics CHO-FORM 5538 Conductive Form-In-Place Gaskets
- Chesterton ARC CS2 Low-viscosity, Composite concrete primer sealer
Copyright © lookpolymers.com All Rights Reserved