SABIC Innovative Plastics LNP VERTON UX06451 BK8-312 PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON UX06451 BK8-312 PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* UX06451 BK8-312 is a compound based on Polyphthalamide resin containing Long Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm @Time 86400 sec |
0.00060 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| 244 MPa | 35400 psi | ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.6 % | 1.6 % | ASTM D638 | |
| Tensile Modulus | 18.6 GPa | 2700 ksi | 1 mm/min; ISO 527 |
| 19.78 GPa | 2869 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 335 MPa | 48600 psi | ISO 178 |
| Flexural Modulus | 17.5 GPa | 2540 ksi | ISO 178 |
| Izod Impact, Notched | 3.09 J/cm | 5.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.23 J/cm | 17.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 13.0 J | 9.59 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
Users viewing this material also viewed the following:
- Nylene® Mach 6 , Fast Cycle Nylon 6
- Plenco 50030 PET, Pellet, Injection Molded, White (discontinued **)
- 3M Dyneon™ CC174-N PTFE, 15% Fiberglass/Moly Filled (discontinued **)
- Chevron Phillips Ryton® P-4 Polyphenylene Sulfide Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8135/GN PEEK, unreinforced, easy flowing
- A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene
- Hexcel® HexPly® F155 Epoxy Resin, 181 Glass Fabric
- ExxonMobil Mobilarma 798
- ChevronTexaco Canopus® 68
- Arlon LW3015B##-P0 0.030" (0.762 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
Copyright © lookpolymers.com All Rights Reserved