SABIC Innovative Plastics LNP Thermocomp PH0700B PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PH0700B PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* PH0700B is a Nylon 6 base resin containing Tungsten. Characteristics are High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 6.78 g/cc | 0.245 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.090 % @Time 86400 sec |
0.090 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 10.5 % | 10.5 % | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Yield | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 6.86 GPa | 995 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.86 GPa | 560 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.06 J/cm @Temperature 23.0 °C |
1.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.88 J/cm @Temperature 23.0 °C |
16.6 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 77.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 183 °C @Thickness 3.20 mm |
361 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Murtfeldt Murinit® SP Polyphenylene Sulfide
- Kennametal Stellite Stellite® SF12 Cobalt Alloy
- Teknor Apex APEX® 96-A0914K-106 Polyvinyl Chloride, Flexible
- Struktol VM 512 LUBRICANT ADDITIVE FOR PVC AND POLYMER PROCESSING
- Trimay® Wear Plate TWP170 Flux Cored Weld Wire & Electrode
- Elektro-Isola Etronit IIQ Phenolic, Paper Reinforcement, Dark Brown, Sheets
- Cytec Thornel® T-50 3K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Armstrong A-12 Epoxy Adhesive, at 2:3 Mix Ratio
- Alloy Wire International RW 122 Hot Cutting Wire - High Strength
Copyright © lookpolymers.com All Rights Reserved