- SABIC Innovative Plastics LNP Thermocomp GC006XXZ PSU
SABIC Innovative Plastics LNP Thermocomp GC006XXZ PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp GC006XXZ PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* GC006XXZ is a compound based on Polysulfone resin containing Carbon Fiber.This product is also known as Thermocomp* GC-1006.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| 1.37 g/cc | 0.0495 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.00040 - 0.00060 cm/cm @Time 86400 sec |
0.00040 - 0.00060 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0025 - 0.0040 cm/cm @Time 86400 sec |
0.0025 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | 5 mm/min; ISO 527 |
| 137 MPa | 19900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 104 MPa | 15100 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D 638 |
| 1.2 % | 1.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 21.54 GPa | 3124 ksi | 1 mm/min; ISO 527 |
| 35.16 GPa | 5100 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 191 MPa | 27700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 16.13 GPa | 2339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 16.25 GPa | 2357 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.90 J/cm @Temperature 23.0 °C |
7.31 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 32.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 184 °C @Thickness 3.20 mm |
363 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 178 °C @Thickness 3.20 mm |
352 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B70 G45 BK Polyamide 6 (Nylon 6)
- Lord Adhesives Flocklok® 850 Flock Adhesive
- Techmer ES HiFill FR® PA6 FR 544
- Goodfellow Molybdenum 90/Titanium 10 Alloy
- EMS-Grivory Grivory® TR 90 PAMACM12
- Ensinger Tecatron® XP-69 Compression Molded PPS Compound, 35% Fiberglass and Mineral Filled
- ExxonMobil Teresstic N Series 150
- Loctite® CHIPBONDER® 3619 Low Temperature Cure, Syringe Dispense
- Kennametal Stellite Deloro® N-6 PM cast
Copyright © lookpolymers.com All Rights Reserved