SABIC Innovative Plastics LNP THERMOCOMP UX93847 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UX93847 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UX93847 is a compound based on Polyphthalamide resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 15.43 GPa | 2238 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM D790 |
| Flexural Modulus | 12.84 GPa | 1862 ksi | ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.93 J/cm | 14.9 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C @Thickness 3.20 mm |
511 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Chemicals Grade A Barium Hydroxide Octahydrate
- SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific)
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 40 lb
- Hexcel® Redux® 335K Adhesive film for bonding metallic and composite components (0.03 psf)
- ExxonMobil Bicor™ 26MB768 OPP Film
- DuPont Performance Polymers Delrin® PC699 NC010 Acetal (POM) (Unverified Data**)
- Arlon R35551X015 0.015" Uncured Silicone Rubber with Woven Fabric Substrate
- A. Schulman POLYBATCH™ Green 30424 Concentrate Based In Polyethylene
- PolyOne Syncure™ System S110FV-UV Polyethylene, Crosslinked (XLPE)
Copyright © lookpolymers.com All Rights Reserved