SABIC Innovative Plastics LNP THERMOCOMP OF008AH PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF008AH PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OF008AH is a compound based on PPS - Branched resin containing 40% Glass Fiber. Added features of this grade are: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| 178 MPa | 25800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| 248 MPa | 36000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 13.4 GPa | 1940 ksi | 2 mm/min; ISO 178 |
| 14.26 GPa | 2068 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.66 | 0.66 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.87 | 0.87 | ASTM D3702 Modified |
| K (wear) Factor | 483 x 10-8 mm³/N-M | 240 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.450 mm |
V-0 @Thickness 0.0177 in |
UL 94 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S80D Silicone Rubber
- Parker Chomerics CHO-SHIELD® 4916 Conductive Coating
- Solvay Specialty Polymers Amodel® A-1133 DW Polyphthalamide (PPA) (discontinued **)
- LG Chemical SEETEC H7511 Polypropylene, Homopolymer
- Henkel Turco T-4181L Liquid Alkaline Rust Remover
- Colorite Polymers 10013G-015 (Molding) Radiation Sterilizable Vinyl Compound
- Arkema Group Rilsan® Fine Powders Natural Polyamide 11
- BASF Ultramid® 1000-11 NF2001 PA66 (Dry)
- PolyOne Edgetek® AM 33 GF/000 L HS Black Polyphthalamide (PPA), Glass Filled (discontinued **)
- SABIC Innovative Plastics LNP THERMOTUF PF00AIS PA 6
Copyright © lookpolymers.com All Rights Reserved