SABIC Innovative Plastics LNP THERMOCOMP LC00APXQ PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LC00APXQ PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LC00APXQ is a compound based on Polyetheretherketone resin containing 50% Carbon Fiber. Added features of this material include: Exceptional Processing, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0013 - 0.0025 cm/cm @Time 86400 sec |
0.0013 - 0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.013 cm/cm @Time 86400 sec |
0.0060 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 320 MPa | 46400 psi | 5 mm/min; ISO 527 |
| 328 MPa | 47600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 47.4 GPa | 6870 ksi | 1 mm/min; ISO 527 |
| 49.8 GPa | 7220 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 473 MPa | 68600 psi | ISO 178 |
| 505 MPa | 73200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 40.5 GPa | 5870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 40.73 GPa | 5907 ksi | 2 mm/min; ISO 178 | |
| Poissons Ratio | 0.45 | 0.45 | ASTM E 132 |
| Shear Modulus | 5.187 GPa | 752.3 ksi | ASTM C273 |
| Shear Strength | 114 MPa | 16500 psi | ASTM C273 |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.68 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 2.00 µm/m-°C @Temperature -40.0 - 150 °C |
1.11 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C @Temperature -40.0 - 150 °C |
11.1 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 335 °C @Thickness 3.20 mm |
635 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Rogers Corporation Ultralam® 3850 Liquid Crystalline Polymer Circuit Material
- LNP Konduit® OTF-212-11 Polyphenylene Sulfide, Proprietary Filler (discontinued **)
- Lubrizol Advanced Materials PEARLTHANE® 11T92E Thermoplastic Polyurethane Elastomer
- Solvay ALKAMULS® A 9 Surfactant
- Solvay SOPROPHOR® CY/8 Surfactant
- Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66
- Cossa Polimeri ESTACARB 1001 Polycarbonate
- DuPont Performance Polymers Crastin® S610SF NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)<
- Addiplast Addilene PMD 50272 Flame Retardant Polypropylene
- 3M 9626 Adhesive Transfer Tape with Quick Bonding Adhesive 360
Copyright © lookpolymers.com All Rights Reserved