SABIC Innovative Plastics LNP THERMOCOMP JF006 PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP JF006 PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* JF006 is a compound based on Polyethersulfone resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 10 - 20 g/10 min

@Load 10.0 kg,
Temperature 345 °C
 10 - 20 g/10 min

@Load 22.0 lb,
Temperature 653 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 142 MPa
20600 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Flexural Strength 192 MPa
27800 psi
2 mm/min; ISO 178
Flexural Modulus 8.20 GPa
1190 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.500 mm
 V-0

@Thickness 0.0197 in
 UL 94