SABIC Innovative Plastics LNP THERMOCOMP DF008 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF008 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF008 is a compound based on Polycarbonate resin containing 40% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | 5 mm/min; ISO 527 |
| 141 MPa | 20500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 |
| 6.9 % | 6.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 14.35 GPa | 2081 ksi | 1 mm/min; ISO 527 |
| 22.44 GPa | 3255 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.19 GPa | 1623 ksi | 2 mm/min; ISO 178 |
| 11.56 GPa | 1677 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.50 J/cm | 2.81 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.22 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 134 °C @Thickness 3.20 mm |
273 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Mitsubishi Hostaphan® WN, 250 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film
- Lubriplate 930-AAA Bentone Type Multi-Purpose Grease
- Struktol V-PETS Processing Additive
- Master Bond Mastersil 726 Conductive Silicone Compound for Heat Transfer
- Chevron Phillips Marlex® 4538A LDPE Blow Molding Resin
- Dow Corning Z-1213 N-PROPYLTRICHLOROSILANE
- Arlon 0.015" (0.381 mm) Flexible Heater Silicone with Fiberglass Substrate (51576R015)
- Ashley Polymers Ashlene® LT940H Nylon 11
- Latrobe Nitralloy® 135 Modified VAC-ARC, 3 to 5 in Premium Nitriding Steel
Copyright © lookpolymers.com All Rights Reserved