| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Noryl_FMC3008A PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* Noryl_FMC3008A compound is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated. Property values at 20% weight reduction, 0.250"" wall.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | foam molded; ASTM D792 |
| 1.28 g/cc | 1.28 g/cc | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa @Thickness 6.35 mm |
6960 psi @Thickness 0.250 in |
ASTM D638 |
| Elongation at Break | 3.5 % @Thickness 6.35 mm |
3.5 % @Thickness 0.250 in |
ASTM D638 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 6.4 mm; ASTM D790 |
| Flexural Modulus | 7.79 GPa | 1130 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Unnotched | 1.01 J/cm @Thickness 6.40 mm |
1.89 ft-lb/in @Thickness 0.252 in |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 3.98 mm |
V-0 @Thickness 0.157 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - Flame Class Minimum Density | 1.15g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 20% |
Users viewing this material also viewed the following:
- PolyOne Edgetek® PS-20CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinued **)
- LG Chemical Lupoy 3010-10 Polycarbonate Resin
- Multibase Multi-Flex® TPE A 5501 LC GREY
- Isoflon PVC Polyvinyl Chloride
- LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP DX06408 PC
- SABIC Innovative Plastics LNP THERMOCOMP JX97000 PES (Europe-Africa-Middle East)
- ATI Allvac® Vasco® X-2M Specialty Steel, Heat Treatment: 899°C (1650°F) Normalization
Copyright © lookpolymers.com All Rights Reserved