SABIC Innovative Plastics LNP STAT-KON DX09315C PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX09315C PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* DX09315C is carbon fiber filled polycarbonate composite with good flow ability, and high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 26 g/10 min @Load 2.16 kg, Temperature 300 °C |
26 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 9.81 GPa | 1420 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 201 MPa | 29200 psi | ASTM D790 |
| Flexural Modulus | 8.13 GPa | 1180 ksi | ASTM D790 |
| Izod Impact, Notched | 0.940 J/cm | 1.76 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.32 J/cm | 13.7 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.22 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 500000 ohm | 10000 - 500000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- H.C. Starck Grade B Yttrium Oxide
- Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
- Lushan VB517 Adhesive Resin for Aluminum-Plastic Composite Panel (ACP), High Temperature
- H.C. Starck Amperit® 703.053 Chromium Oxide (Cr2O3) 99.5%
- SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific)
- Master Bond EP37-3FLF Low Exotherm Highly Flexible Two Component Epoxy
- Polyram RamShine PVS701 AES, UV Stabilized
- BCC Products BC 7053 Epoxy Casting
- Techmer ES Luriblend® HTN 01410 BK
- Kraton® G1702 H (SEP) Linear Diblock Copolymer
Copyright © lookpolymers.com All Rights Reserved