SABIC Innovative Plastics LNP STAT-KON DX00887C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX00887C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX00887C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.320 % | 0.320 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0076 cm/cm @Time 86400 sec |
0.0076 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D638 |
| 59.0 MPa | 8560 psi | ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527 |
| 58.0 MPa | 8410 psi | ASTM D638 | |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 |
| 10.2 % | 10.2 % | ASTM D638 | |
| Elongation at Yield | 4.7 % | 4.7 % | ASTM D638 |
| 9.0 % | 9.0 % | ISO 527 | |
| Tensile Modulus | 2.77 GPa | 402 ksi | 50 mm/min; ASTM D638 |
| 2.84 GPa | 412 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 83.0 MPa | 12000 psi | ISO 178 |
| 101 MPa | 14600 psi | ASTM D790 | |
| Flexural Modulus | 2.81 GPa | 408 ksi | ISO 178 |
| 2.99 GPa | 434 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.23 J/cm | 30.41 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 123 kJ/m² | 58.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 27.0 J | 19.9 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.300 µm/m-°C @Temperature -40.0 - 40.0 °C |
0.167 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 0.300 µm/m-°C @Temperature -40.0 - 40.0 °C |
0.167 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 57.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 57.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
32.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 HF OG General Purpose Acrylic Resin
- Northstar Polymers MAP-R06C Semi Rigid Structural Foam Formulation
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.5 PHR Thanecure ZM
- ExxonMobil PP7043L1 Polypropylene Impact Copolymer
- Beijing Chemical Industry KAIFA® 551-GT30S PBT Resin
- 3M N-200J Adhesion Promoter
- DuPont™ Surlyn® 1825 Zinc Ionomer
Copyright © lookpolymers.com All Rights Reserved