SABIC Innovative Plastics LNP STAT-KON DEL36 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL36 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DEL36 is a compound based on Polycarbonate resin containing 30% Carbon Fiber, 15% PTFE. Added features include: Electrically Conductive, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00020 - 0.00040 cm/cm @Time 86400 sec |
0.00020 - 0.00040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | Type I, 5 mm/min; ASTM D638 |
| 123 MPa | 17800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 |
| 1.5 % | 1.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 15.74 GPa | 2283 ksi | 1 mm/min; ISO 527 |
| 21.22 GPa | 3078 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 184 MPa | 26700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 193 MPa | 28000 psi | ISO 178 | |
| Flexural Modulus | 13.3 GPa | 1930 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 14.39 GPa | 2087 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.730 J/cm | 1.37 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.75 J/cm | 8.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
9.11 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 37.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP66GF50 Nylon 66
- Pacific Sintered Materials FN-255-S Nickel Steel Powdered Metal
- Chevron Phillips 7109LT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
- Williams Advanced Alloys WS327 Solder
- Eifeler Coatings Technology VARIANTIC® TiAlCN PVD Coating
- Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH
- Cotronics Duralco™ 128 500°F (260°C) Ceramic Filled Epoxy
- Asahi Kasei Tenac® GN705 Homopolymer Acetal Resin
- ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved