 POLYMER SEARCH

SABIC Innovative Plastics LNP STAT-KON DEL329XF PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DEL329XF PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DEL329XF is a compound based on Polycarbonate resin containing 10% Carbon Fiber, 15% PTFE. Added features include: Electrically Conductive. Wear Resistant, Flame Retardant.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
1.36 g/cc
0.0491 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
50% RH, 24 hrs; ASTM D570
0.140 %
0.140 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Time 86400 sec
 0.0010 - 0.0020 in/in

@Time 24.0 hour
 ASTM D955
0.0014 - 0.0019 cm/cm

@Time 86400 sec
 0.0014 - 0.0019 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0040 - 0.0050 cm/cm

@Time 86400 sec
 0.0040 - 0.0050 in/in

@Time 24.0 hour
 ASTM D955
0.0045 - 0.0052 cm/cm

@Time 86400 sec
 0.0045 - 0.0052 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 91.0 MPa
13200 psi
ASTM D638
94.0 MPa
13600 psi
ISO 527
Elongation at Break 1.9 %
1.9 %
ISO 527
2.0 %
2.0 %
ASTM D638
Tensile Modulus 7.17 GPa
1040 ksi
50 mm/min; ASTM D638
7.30 GPa
1060 ksi
1 mm/min; ISO 527
Flexural Strength 138 MPa
20000 psi
ASTM D790
139 MPa
20200 psi
ISO 178
Flexural Modulus 6.48 GPa
940 ksi
ASTM D790
7.30 GPa
1060 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.15 J/cm
5.90 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 22.0 kJ/m²
10.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
24.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 41.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
41.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
143 °C

@Thickness 3.20 mm
 289 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
139 °C

@Thickness 3.20 mm
 282 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257
Users viewing this material also viewed the following: