SABIC Innovative Plastics LNP LUBRICOMP UX96507 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UX96507 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UX96507 is a compound based on PPA containing proprietary fillers. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.290 % | 0.290 % | 50% RH, 24 hrs; ASTM D570 |
| 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00010 - 0.00030 cm/cm @Time 86400 sec |
0.00010 - 0.00030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 226 MPa | 32800 psi | Type I, 5 mm/min; ASTM D638 |
| 226 MPa | 32800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 18.73 GPa | 2717 ksi | 1 mm/min; ISO 527 |
| 19.34 GPa | 2805 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 311 MPa | 45100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 313 MPa | 45400 psi | ISO 178 | |
| Flexural Modulus | 16.77 GPa | 2432 ksi | 2 mm/min; ISO 178 |
| 16.9 GPa | 2450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.83 J/cm | 10.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 3.20 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 277 °C | 531 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 280 °C @Thickness 3.20 mm |
536 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 262 °C @Thickness 3.20 mm |
504 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRILOY RF203XXH PA 66
- Teknor Apex Telcar® TL-6075 Thermoplastic Elastomer
- Universal Wire Works 308L Stainless Steel Electrode
- A. Schulman POLYPUR™ FPU 1376 Thermoplastic Polyurethane Compound
- Polyram RamLloy PA917G4 PP/NYLON 66 alloy, 20% Glass Fiber
- TIMCAL TIMREX® T150-600 Primary Synthetic Graphite
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR MBT
- ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 2.9% Cold Work
- 3M FM01N Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved