SABIC Innovative Plastics LNP LUBRICOMP LCL33EXQ PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP LCL33EXQ PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Melt Index of Compound | 30 g/10 min @Load 5.00 kg, Temperature 300 °C |
30 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 181 MPa | 26300 psi | 5 mm/min; ISO 527 |
| 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.96 GPa | 2025 ksi | 1 mm/min; ISO 527 |
| 16.0 GPa | 2320 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 276 MPa | 40000 psi | ISO 178 |
| 277 MPa | 40200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 13.4 GPa | 1940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 13.53 GPa | 1962 ksi | 2 mm/min; ISO 178 | |
| Poissons Ratio | 0.43 | 0.43 | ISO 527-1/2 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 32.0 °C @Thickness 3.20 mm |
89.6 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 875L (FG) Synthetic Oil
- SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific)
- Pearl Engineering PEPLPET F097HA Film Grade Resin
- DSM Arnitel® UM622 Polyether Ester Elastomer (European Grade) (discontinued **)
- Indium Corp. Indalloy 21 Bismuth Solder Alloy
- Karina E 18/10-GIN Gray Aluminum MB (SP31454) for PVC
- ITW Devcon Rubber Repair / Castable Urethane Cable Cast FR, Black
- SABIC Innovative Plastics Valox® 420SE0U PBT (Asia Pacific)
- Eurotec® Tecomid® NA40 GR50 NL RM PA6.6, 50% glass fiber reinforced, MoS2 modified, natural
- Amco PRIMATOP HDPE 002955 Phillips Process Hexene Copolymer
Copyright © lookpolymers.com All Rights Reserved