SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 118 MPa | 17100 psi | ISO 527 |
| 123 MPa | 17800 psi | ASTM D638 | |
| Tensile Strength, Yield | 118 MPa | 17100 psi | ISO 527 |
| 123 MPa | 17800 psi | ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| 2.8 % | 2.8 % | ASTM D638 | |
| Elongation at Yield | 2.6 % | 2.6 % | ASTM D638 |
| 2.6 % | 2.6 % | ISO 527 | |
| Tensile Modulus | 9.08 GPa | 1320 ksi | 1 mm/min; ISO 527 |
| 9.58 GPa | 1390 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| 186 MPa | 27000 psi | ASTM D790 | |
| Flexural Modulus | 8.34 GPa | 1210 ksi | ISO 178 |
| 8.61 GPa | 1250 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.97 J/cm | 3.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.23 J/cm | 17.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.41 | 0.41 | ASTM D3702 Modified |
| K (wear) Factor | 44.3 x 10-8 mm³/N-M | 22.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ PC GR30 Glass Reinforced Polycarbonate
- 3M Dyneon™ CCX1029 PTFE, 10% Carbon Fiber Filled (discontinued **)
- Karina 750D10/120-IS-PO White PVC Compound
- SABIC Innovative Plastics Valox® VIC4350 PBT (Asia Pacific)
- CP-Polymer-Technik Wellamid® 6600 GV 30 HW 30% Glass Fiber Nylon 66, Heat Stabilized, Dry
- Arkema Group LOTADER® 4720 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC
- Overview of materials for Polybutylene Terephthalate (PBT), Aramid Fiber Filled
Copyright © lookpolymers.com All Rights Reserved