SABIC Innovative Plastics LNP COLORCOMP J1000AE PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP J1000AE PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* J1000AE is an unfilled Polyethersulfone. Added feature of this grade is: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.69 GPa | 390 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 125 MPa | 18100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.75e+15 ohm-cm | 1.75e+15 ohm-cm | ASTM D257 |
| Dissipation Factor | 0.0017 @Frequency 50.0 - 60.0 Hz |
0.0017 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.0022 @Frequency 1000 Hz |
0.0022 @Frequency 1000 Hz |
ASTM D150 | |
| 0.0056 @Frequency 1.00e+6 Hz |
0.0056 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Chopped Molding Compound Reinforced
- Resin Technology Group Fusion 543 Ultra Performance Fusion Cyanoacrylate
- Momentive Performance Materials RTV102 White Adhesive Sealant, High Strength Paste
- SABIC Innovative Plastics LNP THERMOCOMP DF0029R PC (Europe-Africa-Middle East)
- Teknor Apex APEX® 4855-LF Polyvinyl Chloride, Flexible
- ChevronTexaco Delo® Extended Life Coolant System, Prediluted 50/50
- 3A Composites Core Materials AIREX® PXc.245 Fiber-Reinforced Structural Foam
- Buckeye Polymers BP RPP 4010 TP Blk Reprocessed Polypropylene, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved