Rogers Corporation Bisco® EC-2040 Conductive Silicone

Category Polymer , Thermoset , Silicone
Manufacturer Rogers Corporation
Trade Name Bisco®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation Bisco® EC-2040 Conductive Silicone.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Base Polymer: SiliconeFiller: Nickel-GraphiteApplications: Silicone EMI ShieldsThickness: 0.020 inches and 0.031 inchesInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Specific Gravity 2.18 g/cc
2.18 g/cc
Thickness 508 - 787 microns
20.0 - 31.0 mil
Range of Thicknesses Available
Mechanical Properties Metric English Comments
Hardness, Shore A 40
40
ASTM D2240
Hardness, Shore OO 85
85
ASTM D2240
Tensile Strength >= 0.621 MPa
>= 90.0 psi
ASTM D142
Elongation at Break <= 60 %
<= 60 %
ASTM D412
Compression Set 3.0 %

@Temperature 70.0 °C
 3.0 %

@Temperature 158 °F
 % of thickness; ASTM D3574
6.0 %

@Temperature 100 °C
 6.0 %

@Temperature 212 °F
 % of thickness; ASTM D395 Method B
12 %

@Temperature 70.0 °C
 12 %

@Temperature 158 °F
 % of deflection; ASTM D3574
22 %

@Temperature 100 °C
 22 %

@Temperature 212 °F
 % of deflection; ASTM D395 Method B
Electrical Properties Metric English Comments
Volume Resistivity 0.20 ohm-cm
0.20 ohm-cm
Rogers Corp. Internal
Shielding Effectiveness 85 dB

@Thickness 0.508 mm,
Frequency 1.00e+10 Hz
 85 dB

@Thickness 0.0200 in,
Frequency 1.00e+10 Hz
 MIL G83528
110 dB

@Thickness 0.508 mm,
Frequency 1.00e+9 Hz
 110 dB

@Thickness 0.0200 in,
Frequency 1.00e+9 Hz
 MIL G83528
120 dB

@Thickness 0.508 mm,
Frequency 1.00e+8 Hz
 120 dB

@Thickness 0.0200 in,
Frequency 1.00e+8 Hz
 MIL G83528
120 dB

@Thickness 0.508 mm,
Frequency 5.00e+8 Hz
 120 dB

@Thickness 0.0200 in,
Frequency 5.00e+8 Hz
 MIL G83528