Ravago Manufacturing Americas Hylex® P1010G40FRMA Polycarbonate, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1010G40FRMA Polycarbonate, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 40% Glass Filled, Flame RetardantInformation provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 185.0 MPa | 26830 psi | ASTM D790 |
| Flexural Modulus | 9.500 GPa | 1378 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Vicat Softening Point | 166 °C | 330 °F | ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 - 5VA @Thickness 3.00 mm |
V-0 - 5VA @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF1030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- ExxonMobil LL 8455.24 Rotational Molding Resin (discontinued **)
- Gharda Chemicals G-PAEKâ„¢ 1230CF Ultra High Performance PEK Polymer
- Haynes 242® alloy, cold rolled sheet, annealed and aged
- Styron Buna® SB 1723 Schkopau Cold Polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- Sumitomo Bakelite Durez® 25378 Phenolic, Injection Grade
- TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al); Aged at 482°C
- AorTech Biomaterials Elast-Eon™ E5-130 Biomedical Polyurethane Pellets
- SABIC Innovative Plastics LNP Stat-kon MD000IU PP
Copyright © lookpolymers.com All Rights Reserved