Quadrant EPP Ketron® 1000 IM Injection Molded Unfilled Polyetheretherketone (ASTM Product Data Sheet)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Ketron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Ketron® 1000 IM Injection Molded Unfilled Polyetheretherketone (ASTM Product Data Sheet).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent chemical resistance Very low moisture absorption Inherently good wear and abrasion resistance Unaffected by continuous exposure to hot water or steam
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ASTM D 570(2) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 107 | 107 | ASTM D785 |
| Hardness, Rockwell R | 127 | 127 | ASTM D785 |
| Hardness, Shore D | 88 | 88 | ASTM D2240 |
| Tensile Strength | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Compressive Strength | 138 MPa | 20000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 2.93 GPa | 425 ksi | ASTM D695 |
| Izod Impact, Notched | 0.21 J/cm | 0.40 ft-lb/in | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | Dry vs. Steel; QTM55007 |
| K (wear) Factor | 755 x 10-8 mm³/N-M | 375 x 10-10 in³-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 0.298 MPa-m/sec | 8500 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 46.8 µm/m-°C @Temperature -40.0 - 150 °C |
26.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E831 |
| Thermal Conductivity | 0.252 W/m-K | 1.75 BTU-in/hr-ft²-°F | ASTM E1530-11 |
| Melting Point | 340 °C | 644 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 249 °C | 480 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/8 inch (Estimated Rating) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | >= 1e+13 ohm | >= 1e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | Short Term; ASTM D149 |
| Dissipation Factor | 0.003 @Frequency 1e+6 Hz |
0.003 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GPP™ 1005M-EX10 Natural PP
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 5 wt% Multi-Wall Carbon Nanotubes
- Dielectric Polymers NT-9511-2 High Tack Tape (discontinued **)
- Total PSC 525 Polystyrene
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- Covestro Bayblend® FR 86 Polycarbonate/ABS Blend
- DuPont™ Surlyn® E185SB Ionomer Resin
- E-Polymers TEKAMID® TA210F Fast Crystallinity PA66, DAM
- ATI Allvac® Vasco® 317 L UNS S31703 Specialty Steel
- TIMET TIMETAL® 6-2-4-2 (Ti-6Al-2Sn-4Zr-2Mo-0.08Si) Titanium Alloy
Copyright © lookpolymers.com All Rights Reserved