Polymer Industries Polyslick UHMW Rod

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Polymer Industries
Trade Name Polyslick
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Industries Polyslick UHMW Rod.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyslick UHMW Rod exhibits all of the durable qualities of our Polyslick UHMW Sheet making it perfect for the application where sheet stock is not suitable. The material is ideally suited for the manufacture of bushings, bearings, rollers, and augers as there is much less wasted material than if the material was made out of sheet stock. Polyslick UHMW Rod is available in up to 10 inches in diameter and is available out of stock in natural virgin and black reprocessed grades.Information provided by Polymer Industries.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ISO 1183
Water Absorption <= 0.010 %
<= 0.010 %
ISO 62
Viscosity Test 3850 cm³/g
3850 cm³/g
ISO 307, 1157, 1628
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.0 MPa
2470 psi
ISO 527-2/1A
Elongation at Break >= 50 %
>= 50 %
ISO 527-2/1A
Elongation at Yield <= 20 %
<= 20 %
ISO 527-2/1A
Tensile Modulus 0.680 GPa
98.6 ksi
ISO 527-2/1A
Tensile Creep Modulus, 1 hour 430 MPa
62400 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 220 MPa
31900 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear 200 µm/m-°C

@Temperature 20.0 °C
111 µin/in-°F

@Temperature 68.0 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 65.0 °C
149 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 42.0 °C
108 °F
ISO 75-1/-2
Vicat Softening Point 80.0 °C
176 °F
ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
IEC 60093
Dielectric Constant 2.1

@Frequency 100 Hz
2.1

@Frequency 100 Hz
IEC 60250
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 45.0 kV/mm
1140 kV/in
IEC 60243-1
Dissipation Factor 0.00029

@Frequency 100 Hz
0.00029

@Frequency 100 Hz
IEC 60250
0.0010

@Frequency 1e+6 Hz
0.0010

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112