Polykemi AB POLYshine PBT D211 GF10 PBT, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | POLYshine |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYshine PBT D211 GF10 PBT, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | With Flow; ISO 2577 |
| 0.013 cm/cm | 0.013 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 105 MPa | <= 15200 psi | ISO/R527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO/R527 |
| Flexural Strength | <= 150 MPa | <= 21800 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa @Temperature 23.0 °C |
754 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 200 °C @Load 5.001 kg |
392 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Nye Lubricants 374B (RL) Synthetic Oil
- Reade Advanced Materials Iron Chromite (FeO·Cr2O3)
- DuPont Bexloy® AXW507NC010 Modified Ionomer Resin (discontinued **)
- Iran Petrochemical (PCC) EX 4 HM9455 F High Density Polyethylene
- Solvay TECHNYL® A 218G1 V30 Black 34N PA66, 30% glass fiber, Conditioned
- SABIC Innovative Plastics LNP Stat-kon AE0039 ABS (Asia Pacific)
- Techmer ES Luriblend® PA6 CF30 TS15 BK 30% Carbon Filled
- Dow ATTANE™ 4201 Ultra Low Density Polyethylene, Blown Film Grade
- Ashley Polymers Ashlene® 980LS-40G Nylon 612, 40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved