PolyOne Syncure™ System S107FH Polyethylene, Crosslinked (XLPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	Syncure™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Syncure™ System S107FH Polyethylene, Crosslinked (XLPE).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

UL Bullentinized, silane-grafted (2-step) moisture crosslinkable polyethylene system, UL 90°C.NOTE: The above represents Typical Properties measured on 18 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.948 g/cc	0.948 g/cc	ASTM D792
Deformation	10 % @Temperature 131 °C	10 % @Temperature 268 °F	UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	59	59	10 sec; ASTM D2240
	64	64	ASTM D2240
Tensile Strength, Yield	31.0 MPa	4500 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	400 %	400 %	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	125 °C	257 °F	UL Temperature Rating

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.5 @Frequency 1.00e+6 Hz	2.5 @Frequency 1.00e+6 Hz	ASTM D150
Dissipation Factor	0.0020 @Frequency 1.00e+6 Hz	0.0020 @Frequency 1.00e+6 Hz	ASTM D150

Descriptive Properties	Value	Comments
Agency Ratings	CSA, C-22.2, No. 127, Type CL-1251
	UL 758
Catalyst Masterbatch	33%	V-0045G RoHS
Forms	Pellets
Gel Content	72%	ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material	XLPE
Generic Name	Polyethylene, Crosslinked (XLPE)
Grafted Base Resin	67%	S-1054A
Processing Method	Extrusion Coating
Regional Availability	North America
Retention of Tensile Elongation	75%	158°C, 1.91 mm; 672 hr, UL Standard
Retention of Tensile Strength	75%	158°C, 1.91 mm; 672 hr, UL Standard
Uses	Appliances
	Wire & Cable Applications
Wire Types	AWM