PolyOne Syncure™ System S100FH Polyethylene, Crosslinked (XLPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	Syncure™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Syncure™ System S100FH Polyethylene, Crosslinked (XLPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Syncure™ systems are two part moisture crosslinkable compounds. S100FH is a UL bulletinized, flame retardant cable insulation compound. Available in a RoHS compliant version.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.01 g/cc	1.01 g/cc	ASTM D792
Deformation	10 % @Temperature 131 °C, Time 3600 sec	10 % @Temperature 268 °F, Time 1.00 hour	500 g; UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	47	47	10 sec; ASTM D2240
	53	53	ASTM D2240
Tensile Strength, Yield	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	400 %	400 %	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	90.0 °C	194 °F	UL Temperature Rating

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.31 @Frequency 1.00e+7 Hz	2.31 @Frequency 1.00e+7 Hz	ASTM D150
Dielectric Strength	39.0 kV/mm	991 kV/in	ASTM D149
Dissipation Factor	0.0012 @Frequency 1.00e+7 Hz	0.0012 @Frequency 1.00e+7 Hz	ASTM D150

Descriptive Properties	Value	Comments
Agency Ratings	MIL C-24643
	UL 44
Appearance	Natural Color
Catalyst Masterbatch	17%	V-0022G RoHS
Features	Flame Retardant
	Oil Resistant
Flame Test	Pass	CSA FT-2; Horizontal
	Pass	UL 1581; Horizontal
Forms	Pellets
Gel Content	68%	ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material	XLPE
Generic Name	Polyethylene, Crosslinked (XLPE)
Grafted Base Resin	83%	S-1054A
Processing Method	Extrusion Coating
Regional Availability	North America
Retention of Tensile Elongation	90%	121°C, 1.91 mm; UL Standard, 336 hrs.
Retention of Tensile Strength	95%	121°C, 1.91 mm; UL Standard, 336 hrs.
Uses	Wire & Cable Applications
Wire Types	RHH
	RHW-2
	SIS
	USE-2
	XHH
	XHHW