PolyOne OnFlex™ HT 60A-3S2101 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name OnFlex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne OnFlex™ HT 60A-3S2101 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ HT compounds are in compliance with EN 681-2 and offer excellent mechanical properties, a wide hardness range and good processability.Properties are measured using injection molded plaques.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
IRHD; ISO 48
60

@Temperature 23.0 °C
60

@Temperature 73.4 °F
Injection Molded; DIN 53505
Tensile Strength at Break 7.90 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
1150 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
200 mm/min Flow; DIN 53504
10.5 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
1520 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
200 mm/min Across Flow; DIN 53504
Elongation at Break 650 %

@Thickness 2.00 mm,
Temperature 23.0 °C
650 %

@Thickness 0.0787 in,
Temperature 73.4 °F
200 mm/min Flow; DIN 53504
840 %

@Thickness 2.00 mm,
Temperature 23.0 °C
840 %

@Thickness 0.0787 in,
Temperature 73.4 °F
200 mm/min Across Flow; DIN 53504
Compression Set 24 %

@Temperature 23.0 °C,
Time 79200 sec
24 %

@Temperature 73.4 °F,
Time 22.0 hour
ISO 815
33 %

@Temperature 70.0 °C,
Time 79200 sec
33 %

@Temperature 158 °F,
Time 22.0 hour
ISO 815
42 %

@Temperature 100 °C,
Time 79200 sec
42 %

@Temperature 212 °F,
Time 22.0 hour
ISO 815
43 %

@Temperature 125 °C,
Time 79200 sec
43 %

@Temperature 257 °F,
Time 22.0 hour
ISO 815
46 %

@Temperature -10.0 °C,
Time 259000 sec
46 %

@Temperature 14.0 °F,
Time 72.0 hour
ISO 815
65 %

@Temperature 150 °C,
Time 79200 sec
65 %

@Temperature 302 °F,
Time 22.0 hour
ISO 815
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Descriptive Properties Value Comments
Change in Shore Hardness in Air -3 Shore A
DIN 53505; Shore A, 70°C, 168 hr
Change in Tensile Strain at Break in Air -0.9%
DIN 53504; 70°C, 168 hr, 2.00 mm
Change in Tensile Strength in Air -0.5%
DIN 53504; 70°C, 168 hr, 2.00 mm
Change in Volume 0.2%
ISO 1817; 70°C, 168 hr, in Water
10%
ISO 1817; 70°C, 72 hr, in ASTM #1 Oil
Features High Heat Resistance
Low Compression Set
Ozone Resistant
Forms Pellets
Generic Material TPE
Generic Material Type Styrenic Thermoplastic Elastomer (TES)
Generic Name Thermoplastic Elastomer (TPE)
Injection Rate Fast
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Stress Relaxation 13%
ISO 3384; 23°C; 168hrs, 25% compression, Method A
31%
ISO 3384; 23°C; 100d, 25% compression, Method A
Uses Pipe Seals