PolyOne Maxxam™ PD 40 TF Black Polypropylene Homopolymer (PP Homopolymer)

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	PolyOne Corporation
Trade Name	Maxxam™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Maxxam™ PD 40 TF Black Polypropylene Homopolymer (PP Homopolymer).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.21 g/cc	1.21 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	ASTM D955
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 230 °C	11 g/10 min @Load 4.76 lb, Temperature 446 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	31.0 MPa	4500 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	8.0 %	8.0 %	Type I, 51 mm/min; ASTM D638
Flexural Strength	55.8 MPa	8090 psi	ASTM D790
Flexural Modulus	3.72 GPa	540 ksi	ASTM D790
Izod Impact, Notched	0.270 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.506 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	145 °C @Thickness 3.18 mm	293 °F @Thickness 0.125 in	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Mold Temperature	16.0 - 50.0 °C	60.8 - 122 °F

Descriptive Properties	Value	Comments
Appearance	Black
Features	General Purpose
	Homopolymer
	Industrial Resin
Filler / Reinforcement	Talc Filler, 40% Filler by Weight
Forms	Pellets
Generic Material	PP Homopolymer
Generic Name	Polypropylene Homopolymer (PP Homopolymer)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications