PolyOne Maxxam™ FR MF5420-0013 FR Polypropylene, Unspecified (PP, Unspecified)

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	PolyOne Corporation
Trade Name	Maxxam™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Maxxam™ FR MF5420-0013 FR Polypropylene, Unspecified (PP, Unspecified).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.918 g/cc	0.918 g/cc	ASTM D792
Melt Flow	8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	10.9 MPa	1580 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	90 %	90 %	Type I, 51 mm/min; ASTM D638
Flexural Modulus	0.152 GPa	22.0 ksi	ASTM D790
Izod Impact, Notched	3.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	6.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	41.0 °C @Thickness 3.18 mm	106 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	All Color; UL 94
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	All Color; UL 94
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	All Color; UL 94

Descriptive Properties	Value	Comments
Features	Flame Retardant
Forms	Pellets
Generic Material	PP, Unspecified
Generic Name	Polypropylene, Unspecified (PP, Unspecified)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America